Advancing Carbon Fiber Composite Inspection: Deep Learning-Enabled Defect Localization and Sizing via 3-Dimensional U-Net Segmentation of Ultrasonic Data.

Researchers

Journal

Modalities

Models

Abstract

In Non-Destructive Evaluation (NDE), accurately characterizing defects within components relies on accurate sizing and localization to evaluate the severity or criticality of defects. This study presents for the first time a deep learning methodology using 3-Dimensional (3D) U-Net to localize and size defects in Carbon Fibre Reinforced Polymer (CFRP) composites through volumetric segmentation of ultrasonic testing data. Using a previously developed approach, synthetic training data closely representative of experimental data was used for the automatic generation of ground truth segmentation masks. The model’s performance was compared to the conventional amplitude 6 dB drop analysis method used in industry against ultrasonic defect responses from 40 defects fabricated in CFRP components. The results showed good agreement with the 6 dB drop method for in-plane localization and excellent through-thickness localization, with Mean Absolute Errors (MAE) of 0.57 mm and 0.08 mm, respectively. Initial sizing results consistently oversized defects with a 55% higher mean average error than the 6 dB drop method. However, when a correction factor was applied to account for variation between the experimental and synthetic domains the final sizing accuracy resulted in a 35% reduction in MAE compared to the 6 dB drop technique. By working with volumetric ultrasonic data (as opposed to 2D images) this approach reduces pre-processing (such as signal gating) and allows for the generation of 3D defect masks which can be used for the generation of computer aided design files; greatly reducing the qualification reporting burden of NDE operators.